Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.16
|
g/cm³
|
ISO 1183 |
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)
|
50.0
|
cm³/10min
|
ISO 1133 |
Molding Shrinkage
|
ISO 294-4 | ||
Across Flow
|
1.5
|
%
|
|
Flow
|
1.3
|
%
|
|
Water Absorption (Saturation, 23°C)
|
0.70
|
%
|
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH)
|
0.30
|
%
|
ISO 62 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus
|
100
|
MPa
|
ISO 527-2 |
Tensile Stress (Break)
|
25.0
|
MPa
|
ISO 527-2 |
Tensile Stress
|
ISO 527-2 | ||
10% Strain
|
6.10
|
MPa
|
|
100% Strain
|
10.0
|
MPa
|
|
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | ||
-30°C
|
No Break
|
||
23°C
|
No Break
|
||
Notched Izod Impact Strength (23°C)
|
No Break
|
ISO 180/1A | |
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Shore Hardness (Shore D)
|
46
|
ISO 868 | |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Vicat Softening Temperature
|
50.0
|
°C
|
ISO 306/B50 |
Melting Temperature 2
|
185
|
°C
|
ISO 11357-3 |
CLTE - Flow
|
0.00016
|
cm/cm/°C
|
ISO 11359-2 |
CLTE - Transverse
|
0.00016
|
cm/cm/°C
|
ISO 11359-2 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Volume Resistivity
|
1.0E+13
|
ohm·cm
|
IEC 60093 |
Electric Strength
|
20
|
kV/mm
|
IEC 60243-1 |
Relative Permittivity (1 MHz)
|
4.40
|
IEC 60250 | |
Dissipation Factor (1 MHz)
|
0.035
|
IEC 60250 | |
Comparative Tracking Index
|
600
|
V
|
IEC 60112 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flammability Classification (1.60 mm)
|
HB
|
IEC 60695-11-10, -20 |
抗冲击TPE 荷兰DSM EM460 价格 EM460物性