Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Specific Gravity
|
1.39
|
--
|
g/cm³
|
ASTM D792 |
Molding Shrinkage
|
Internal Method | |||
Across Flow
|
0.90
|
--
|
%
|
|
Flow
|
0.40
|
--
|
%
|
|
Water Absorption (Equilibrium)
|
--
|
1.7
|
%
|
ASTM D570 |
Water Absorption (Equilibrium, 23°C, 50% RH)
|
--
|
1.7
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C)
|
10000
|
8000
|
MPa
|
ISO 527-2 |
Tensile Strength
|
186
|
132
|
MPa
|
ASTM D638 |
Tensile Stress (Break, 23°C)
|
190
|
135
|
MPa
|
ISO 527-2 |
Tensile Elongation (Break)
|
3.0
|
5.0
|
%
|
ASTM D638 |
Tensile Strain (Break, 23°C)
|
3.0
|
5.0
|
%
|
ISO 527-2 |
Flexural Modulus
|
9300
|
6300
|
MPa
|
ASTM D790 |
Flexural Modulus (23°C)
|
9000
|
6800
|
MPa
|
ISO 178 |
Flexural Strength
|
289
|
216
|
MPa
|
ASTM D790 |
Flexural Strength (23°C)
|
280
|
202
|
MPa
|
ISO 178 |
Taber Abrasion Resistance
|
--
|
15.0
|
mg
|
ASTM D1044 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
11
|
16
|
kJ/m²
|
ISO 179 |
Charpy Unnotched Impact Strength
|
72
|
83
|
kJ/m²
|
ISO 179 |
Notched Izod Impact
|
130
|
150
|
J/m
|
ASTM D256 |
Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Rockwell Hardness
|
ASTM D785 | |||
M-Scale
|
96
|
75
|
||
R-Scale
|
120
|
112
|
||
Rockwell Hardness
|
ISO 2039-2 | |||
M-Scale
|
96
|
96
|
||
R-Scale
|
120
|
112
|
||
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
260
|
--
|
°C
|
ASTM D648 |
Heat Deflection Temperature (0.45 MPa, Unannealed)
|
264
|
--
|
°C
|
ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
250
|
--
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
249
|
--
|
°C
|
ISO 75-2/A |
CLTE - Flow
|
0.000030
|
--
|
cm/cm/°C
|
ASTM D696 |
CLTE - Flow
|
0.000030
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Specific Heat
|
1590
|
--
|
J/kg/°C
|
|
Thermal Conductivity
|
0.30
|
--
|
W/m/K
|
|
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+15
|
--
|
ohm
|
IEC 60093 |
Volume Resistivity (23°C)
|
1.0E+15
|
--
|
ohm·cm
|
IEC 60093 |
Electric Strength
|
28
|
--
|
kV/mm
|
IEC 60243-1 |
Comparative Tracking Index (3.00 mm)
|
600
|
--
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating
|
UL 94 | |||
0.794 mm
|
HB
|
--
|
||
1.59 mm
|
HB
|
--
|
||
Oxygen Index
|
23
|
--
|
%
|
ASTM D2863 |
日本旭化成PA66 1300G 价格 英文物性表