Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Specific Gravity |
1.22
|
--
|
g/cm³
|
ASTM D792 |
Density |
1.23
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage - Flow | Internal Method | |||
1.60 mm
|
0.60
|
--
|
%
|
|
3.20 mm
|
0.70
|
--
|
%
|
|
6.40 mm
|
0.90
|
--
|
%
|
|
Molding Shrinkage - Across Flow | Internal Method | |||
1.60 mm
|
1.2
|
--
|
%
|
|
3.20 mm
|
1.4
|
--
|
%
|
|
6.40 mm
|
1.7
|
--
|
%
|
|
Molding Shrinkage | ISO 294-4 | |||
Across Flow: 2.00 mm
|
1.2
|
--
|
%
|
|
Flow: 2.00 mm
|
0.70
|
--
|
%
|
|
Water Absorption (23°C, 24 hr) |
1.7
|
--
|
%
|
ISO 62 |
Water Absorption (Saturation, 23°C) |
7.1
|
--
|
%
|
ASTM D570 |
Water Absorption (Saturation, 23°C) |
7.6
|
--
|
%
|
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) |
2.2
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C) |
5500
|
3500
|
MPa
|
ISO 527-2 |
Tensile Strength (23°C) |
121
|
83.0
|
MPa
|
ASTM D638 |
Tensile Stress (Break, 23°C) |
120
|
75.0
|
MPa
|
ISO 527-2 |
Tensile Elongation (Break, 23°C) |
3.0
|
8.0
|
%
|
ASTM D638 |
Tensile Strain (Break, 23°C) |
3.0
|
13
|
%
|
ISO 527-2 |
Tensile Creep Modulus (1 hr) |
--
|
3300
|
MPa
|
ISO 899-1 |
Tensile Creep Modulus (1000 hr) |
--
|
2200
|
MPa
|
ISO 899-1 |
Flexural Modulus (23°C) |
4830
|
2760
|
MPa
|
ASTM D790 |
Flexural Modulus (23°C) |
4800
|
2900
|
MPa
|
ISO 178 |
Flexural Strength (23°C) |
165
|
--
|
MPa
|
ASTM D790 |
Flexural Strength (23°C) |
190
|
100
|
MPa
|
ISO 178 |
Shear Strength (23°C) |
76.0
|
--
|
MPa
|
ASTM D732 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength | ISO 179/1eA | |||
-40°C
|
4.5
|
4.0
|
kJ/m²
|
|
-30°C
|
4.5
|
4.0
|
kJ/m²
|
|
23°C
|
5.0
|
6.0
|
kJ/m²
|
|
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C
|
40
|
30
|
kJ/m²
|
|
23°C
|
40
|
70
|
kJ/m²
|
|
Notched Izod Impact (23°C) |
48
|
53
|
J/m
|
ASTM D256 |
Notched Izod Impact Strength | ISO 180/1A | |||
-40°C
|
4.5
|
3.0
|
kJ/m²
|
|
-30°C
|
4.5
|
3.0
|
kJ/m²
|
|
23°C
|
4.5
|
4.0
|
kJ/m²
|
|
Unnotched Izod Impact Strength | ISO 180/1U | |||
-30°C
|
35
|
28
|
kJ/m²
|
|
23°C
|
40
|
55
|
kJ/m²
|
|
Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Rockwell Hardness | ASTM D785 | |||
M-Scale
|
95
|
84
|
||
R-Scale
|
122
|
113
|
||
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature (0.45 MPa, Unannealed) |
258
|
--
|
°C
|
ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed) |
243
|
--
|
°C
|
ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed) |
238
|
--
|
°C
|
ISO 75-2/A |
Glass Transition Temperature |
80.0
|
--
|
°C
|
ISO 11357-2 |
Melting Temperature |
263
|
--
|
°C
|
ASTM D3418 |
Melting Temperature 2 |
262
|
--
|
°C
|
ISO 11357-3 |
CLTE - Flow | ASTM E831 | |||
-40 to 23°C
|
0.000042
|
--
|
cm/cm/°C
|
|
23 to 55°C
|
0.000040
|
--
|
cm/cm/°C
|
|
55 to 160°C
|
0.000027
|
--
|
cm/cm/°C
|
|
CLTE - Flow | ISO 11359-2 | |||
-40 to 23°C
|
0.000042
|
--
|
cm/cm/°C
|
|
23 to 55°C
|
0.000040
|
--
|
cm/cm/°C
|
|
55 to 160°C
|
0.000027
|
--
|
cm/cm/°C
|
|
CLTE - Transverse | ASTM E831 | |||
-40 to 23°C
|
0.000077
|
--
|
cm/cm/°C
|
|
23 to 55°C
|
0.000096
|
--
|
cm/cm/°C
|
|
55 to 160°C
|
0.00016
|
--
|
cm/cm/°C
|
|
CLTE - Transverse | ISO 11359-2 | |||
-40 to 23°C
|
0.000077
|
--
|
cm/cm/°C
|
|
23 to 55°C
|
0.000096
|
--
|
cm/cm/°C
|
|
55 to 160°C
|
0.00016
|
--
|
cm/cm/°C
|
|
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Surface Resistivity |
--
|
1.0E+15
|
ohms
|
IEC 60093 |
Volume Resistivity |
1.0E+16
|
--
|
ohm·cm
|
IEC 60093 |
Relative Permittivity | IEC 60250 | |||
23°C, 100 Hz
|
3.90
|
--
|
||
23°C, 1 MHz
|
3.20
|
--
|
||
Dissipation Factor | IEC 60250 | |||
23°C, 100 Hz
|
0.013
|
--
|
||
23°C, 1 MHz
|
0.015
|
--
|
||
Comparative Tracking Index |
> 600
|
--
|
V
|
IEC 60112 |
Electric Strength (23°C, 2.00 mm) |
25
|
--
|
kV/mm
|
IEC 60243-1 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating - UL | UL 94 | |||
0.710 mm
|
HB
|
--
|
||
1.50 mm
|
HB
|
--
|
||
3.00 mm
|
HB
|
--
|
||
Flammability Classification | IEC 60695-11-10, -20 | |||
0.710 mm
|
HB
|
--
|
||
1.50 mm
|
HB
|
--
|
||
3.00 mm
|
HB
|
--
|
||
Glow Wire Flammability Index | IEC 60695-2-12 | |||
0.750 mm
|
650
|
--
|
°C
|
|
1.50 mm
|
650
|
--
|
°C
|
|
3.00 mm
|
800
|
--
|
°C
|
|
Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
0.750 mm
|
675
|
--
|
°C
|
|
1.50 mm
|
675
|
--
|
°C
|
|
3.00 mm
|
675
|
--
|
°C
|
|
Oxygen Index |
24
|
--
|
%
|
ISO 4589-2 |
UL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
RTI Str | UL 746 | |||
0.710 mm
|
125
|
--
|
°C
|
|
1.50 mm
|
125
|
--
|
°C
|
|
3.00 mm
|
125
|
--
|
°C
|
|
RTI Imp | UL 746 | |||
0.710 mm
|
120
|
--
|
°C
|
|
1.50 mm
|
120
|
--
|
°C
|
|
3.00 mm
|
120
|
--
|
°C
|
|
RTI Elec | UL 746 | |||
0.710 mm
|
125
|
--
|
°C
|
|
1.50 mm
|
125
|
--
|
°C
|
|
3.00 mm
|
125
|
--
|
°C
|
|
Comparative Tracking Index (CTI) (3.00 mm) |
> 600
|
--
|
V
|
UL 746 |
Comparative Tracking Index (CTI) (PLC) (3.00 mm) |
PLC 0
|
--
|
UL 746 |
PA66 70G13L价格 70G13L英文物性